退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

Effect of an abrupt change in pulling rate on microstructures of directionally solidified Al2O3-Er3Al5O12 eutectic and off-eutectic composite ceramics

Directionally solidified microstructures of Al₂O₃-Er₃Al₅O₁₂ eutectic and off-eutectic in situ composite ceramics were explored under abrupt-change pulling rate conditions. Corresponding temperature distributions and interface locations were studied. In eutectic composition, fluctuation of eutectic spacing occurred when the pulling rate increased abruptly. A gradually increase or abrupt increase in eutectic spacing was observed when the pulling rate decreased abruptly. In hypoeutectic and hypereutectic compositions, formation of the primary phases were suppressed when the pulling rate increased abruptly from 10?µm/s to 100?µm/s, while primary phases precipitated when the pulling rate decreased abruptly from 100?µm/s to 10?µm/s. The interface altitude decreased after the pulling rate increased abruptly, but increased after the pulling rate decreased abruptly. The liquid composition restriction (around the eutectic composition) at the eutectic interface plays an important role in the suppression of the primary dendrite and coupled eutectic oxides can be obtained in off-eutectic compositions even under higher solidification rate conditions.     

Catalytic Hydrocracking of a Bitumen‐Derived Asphaltene over NiMo/γ‐Al2O3 at Various Temperatures

Hydrocracking of a bitumen‐derived asphaltene over NiMo/γ‐Al₂O₃ was investigated in a microbatch reactor at varying temperatures. The molar kinetics of asphaltene cracking reaction was examined by fitting the experimental data. Below a defined temperature, the molar reaction showed the first‐order kinetic feature while at higher temperatures secondary reactions such as coke formation became significant, causing deviation of the reaction behavior from the proposed first‐order kinetic model. Selectivity analysis proved that dominant products varied from gases to liquids to gases with increasing temperature, shifting the dominant reaction from C–S bonds cleavage to C–C bonds cleavage.     

离子液体水热法辅助合成稀土Ce掺杂ZnO纳米材料的制备及其应用研究

以1-甲基咪唑和氯代正丁烷为原料,合成1-丁基-3-甲基咪唑氯盐离子液体;以醋酸锌[Zn(Ac)2]、硫酸锌(ZnSO4)和氯化锌(ZnCl2)为锌源,在1-丁基-3-甲基咪唑氯盐离子液体和丙氨酸体系中与硝酸铈反应,经水热合成法制备得到Ce掺杂的纳米ZnO。采用扫描电子显微镜(SEM)、紫外-可见光吸收光谱(UV-Vis)、X射线衍射仪(XRD)、X射线光电子能谱分析(XPS)和红外光谱(FT-IR)对产品进行表征。以亚甲基蓝(MB)为目标降解物,采用UV-Vis检测,考察了Ce掺杂的纳米ZnO的光催化活性。研究表明,焙烧温度对光催化的晶体结构和光催化活性产生较大的影响;2%Ce/ZnO、焙烧温度为500℃、催化时间为30 min、亚甲基蓝用量0.05 g、pH值为10时降解率可达99.5%以上。     

焊缝表面缺陷激光扫描三维重构测量

为检测工件焊缝表面缺陷，采用点激光位移传感测距法和数据拟合技术进行焊缝表面缺陷检测试验研究. 首先采集缺陷表面轮廓数据点，利用高斯滤波对原始数据降噪处理. 再对处理后的数据点进行Delaunay三角剖分，使散乱点连接并结合其空间坐标重构出缺陷的三维模型. 结果表明，基于点激光位移传感测距技术及焊缝表面缺陷三维重构方法可以准确判断焊缝成形情况.     

铝碳质长水口用低铝抗氧化涂层的研制

为抑制铝碳质长水口使用过程中石墨的氧化，其表面会涂覆含 20%~30%Al₂O₃的抗氧化涂层，但切割丝钢等特种钢冶炼过程必须严格控制钢液中夹杂的 Al₂O₃的含量，因此需要制备低氧化铝含量的抗氧化涂层。本文通过调节涂料组成、加水量和水玻璃加入量制备了低铝抗氧化涂层，并利用扫描电镜分析了抗氧化实验后试样断口的显微结构。结果表明：以粘土粉、钾长石粉和硅砂为主要原料，添加 10%硼砂的涂料可在 800 ℃形成良好的釉层，此时涂料中 A12O3的含量可降至 12%，得到了低铝涂料；当加入占涂料质量 80%的水和 40%的水玻璃时，涂层具有最佳的涂覆性能和抗氧化性能，涂层和长水口基体结合致密，保护了长水口中的石墨不被氧化。